Nickel 200 Rod

The nickel 200 rod causes resistance to oxidizing acid chlorides like ferric, cupric and mercuric salts, stannic chloride, neutral and alkaline salt and dilute solutions at the atmospheric temperature. In fact under typical exposure conditions its rate of corrosion is less than 5 mpy.

Specification
Rod Size diameter: 3mm above, length: 20mm above

Chemical composition of Nickel 200 Rod
Nickel 99.0%
Copper 0.25%
Iron 0.40%
Manganese 0.35%
Carbon 0.15%
Silicon 0.35%
Sulfur 0.01%

Physical properties of Nickel 200 Rod
Density, g/cm3 8.89
Melting Range, °C 1435-1446
Specific Heat, J/kg•°C 456
Curie Temperature, °C 360

Properties of Nickel 200 Rod
1. Intense resistance to neutral, alkaline and ferric, cupric and mercuric salts
2. Large electrical conductance and Curie Temperature

Applications of Nickel 200 Rod
1. High temperature operations
2. Manufacturing artificial synthetic fibers
3. Chemical Treatment and Preservation
4. Aerospace Industry