Stainless steel 310S wire mesh

The stainless steel 310S wire mesh introduces the enhanced combination of superior elevated temperature features with the refined ductility as well as weldability. The wire mesh is preferably employed in the elevated temperature operations. It offers higher resistance to oxidation up to temperature limits of 1150oC. It retains its hardness even lower than cryogenic temperature and utilized in the certain corrosive conditions like preparation of urea.
Wire Mesh Specification:
Thickness: Aperture: Mesh
0.1mm -10mm 0.05mm above 0.5mesh-250mesh/inch

Chemical composition of Stainless Steel 310S Wire
Carbon 0.25 max 0.08 max
Silicon 1.50 max 1.50 max
Manganese 2.00 max 2.00 max
Phosphorus 0.045 max 0.045 max
Sulphur 0.030 max 0.030 max
Chromium 24.00 - 26.00 24.00 - 26.00
Nickel 19.00 - 22.00 19.00 - 22.00

Physical Properties of 310/310S Stainless Steel Wire
Density 8,000 Kg/m3
Electrical Conductivity 25oC 1.25 %IACS
Electrical Resistivity 25oC 0.78 Micro ohm.m
Modulus of Elasticity 20oC 200 GPa
Shear Modulus 20oC 77 GPa
Specific Heat 500 J/kg.oC

Mechanical Properties of 310/310S Stainless Steel Wire
Grade 0.2 % Proof Stress MPa (min) 205
Tensile Strength MPa (min) 520
Elongation % (min) 40
Hardness (HV) (max) 225

Characteristics of Stainless steel 310S Wire Mesh:
1. Good resistance to aqueous corrosion.
2. Excellent resistance to oxidation and carburization at high temperatures.
3. More resistant to stress corrosion cracking than stainless steel 304.
Applications of Stainless steel 310S Wire Mesh:
1. Furnace Components
2. Oil Burner components
3. Heat Exchangers
4. Carburized boxes